The standard electrode potentials of $Zn^{2+}/Zn$ and $Ag^{+}/Ag$ are $-0.763 \ V$ and $+0.799 \ V$ respectively. The standard potential of the cell is ............ $V$.

Zinc can be coated on iron to produce galvanized iron,but the reverse is not possible. This is because:

The electrode potential for $M^{2+}_{(aq)} + e^- \rightarrow M^{+}_{(aq)}$ and $M^{+}_{(aq)} + e^- \rightarrow M_{(s)}$ are $+0.15 \text{ V}$ and $+0.50 \text{ V}$ respectively. The value of $E^\circ_{M^{2+}/M}$ will be: (in $\text{ V}$)

If the standard reduction potentials of four electrodes $A$, $B$, $C$, and $D$ are $+2.5 \text{ V}$, $+3.0 \text{ V}$, $-2.0 \text{ V}$, and $-1.5 \text{ V}$ respectively, in which of the following cases is the standard $emf$ of the cell maximum?

$I_2 + 2e^{-} \to 2I^{-}$; $E^{o} = 0.54 \ V$
$Cl_2 + 2e^{-} \to 2Cl^{-}$; $E^{o} = 1.36 \ V$
$Mn^{3+} + e^{-} \to Mn^{2+}$; $E^{o} = 1.50 \ V$
$Fe^{3+} + e^{-} \to Fe^{2+}$; $E^{o} = 0.77 \ V$
Which of the following is a correct statement?

The $(\frac{\partial E}{\partial T})_P$ of different types of half cells are as follows:

$A$	$B$	$C$	$D$
$1 \times 10^{-4}$	$2 \times 10^{-4}$	$0.1 \times 10^{-4}$	$0.2 \times 10^{-4}$

(Where $E$ is the electromotive force)
Which of the above half cells would be preferred to be used as reference electrode?